Ultranap - ICOPAL
- category: Roll waterproofing
- Brands: ICOPAL
Ultranap - Roll-fed polymeric-bitumen SBS-modified material is made on a non-woven basis from high durability polyester with fine-grained sand... See more
Ultranap - Roll-fed polymeric-bitumen SBS-modified material is made on a non-woven basis from high durability polyester with fine-grained sand on the top side. On the lower side the material is coated with an easily flammable polyethylene film.
See less
PARAMETER ITEM, MEASURE UNIT |
VALUE |
Width, m |
1 |
Length, m |
10 |
Weight, kg/m2 |
5,0 |
Base |
High durability polyester |
Breaking load under tension, N/50 mm, not less |
1000 |
relative elongation, %, not lower |
45 |
Heat resistance during two hours at the temperature of °С, not lower |
110 |
Radius of curvature with radius at bent 25 mm at the temperature of °С, not above |
- 30 |
Ductile-to-brittle transition temperature of polymeric-bitumen binder at the temperature of °С, not above |
- 40 |
Waterproofing under a pressure 0.2 MPa, not lower, during 24 hours |
No signs of water leak |
Water absorption during 24 hours by weight, %, not above |
1 |
-
reliabilityanddurability;
-
fast mounting;
-
versatility
-
polymeric-bitumen binder strips provide high quality seam welding
-
opportunity to arrange waterproofing of wet concrete that has not gained grade strength
-
biostability
-
economical practicality of single layer solution arrangement
-
high physical and mechanical characteristics;
-
efficient anti-radon protection;
-
resistance to aggressive environments.
APPLICATION AREA
- Arrangement of waterproofing of foundations of various buildings, underground and embedded structures of industrial, civil and transportation construction.
- Waterproofing of water reservoirs, water storages, firewater ponds, industrial dams, irrigation channels, slopes and mounds.
- Arrangement of insulating waterproof carpet of roofs, parking areas, terraces and so called “Green Roofs” that are in use, and arrangement of out-of-use ballasted roofs.
- Arrangement of anti-radon protection of buildings.
- Recommended to be applied by JSC Central Scientific Research Institute of Construction Science and Research Centre «Tunnels and Metropolitans» and Scientific Research Institute of Construction Physics of Russian Academy of Architecture and Construction Sciences.
APPLICATION METHOD
- Horizontal surface. Free application to base.
- Vertical surface. Mechanical mounting to base.
Products offered
delivery
- When purchasing products for up to 100 GEL, the delivery price is 6 GEL;
- When purchasing products in the amount of 100 to 500 GEL, the delivery price is determined on the basis of: 1 km - 1.50 GEL;
- When purchasing products worth more than GEL 500, delivery is free (Tbilisi, Kutaisi, Batumi, Rustavi, Mtskheta); Promotion and free delivery service for purchases over 300₾ are valid at this stage.
- The cost of delivery outside the city is determined at the rate: 1 km - 2 GEL.
Delivery time:
- Tbilisi | Rustavi | Mtskheta | Kutaisi | Batumi
Delivery time: 2-3 working days
- Out of town::
Delivery time: 3-4 days
Note: Delivery is carried out only to the address, without unloading from the car and delivery to the apartment.
Product comparison

Ultranap - ICOPAL
choose a product
- IMPER BALANCE H 3,5 - EPP 3.5 kg / m2, 10 m2
- Vilatex in ECP 2.5 kg/sq.m (1*15m)
- Hydroisol TKP 4.5 (1*10m2)
- Hydroisol TPP 2.5 (1*10m2)
- Syntan Solo vent - ICOPAL
- Vilatex in ECP 4.0 kg/sq.m (1*10m)
- Hydroisol TPP 3.5 (1*10m2)
- Hydroizol TKP 3.2 (1*10m2)
- icopal ultra Н
- villatex В - ICOPAL
- IMPER GARANT B 5.0 - ekp 5 kg / m2, 10 m2
- villatex Н - ICOPAL
- IMPER BALANCE (Т) Н 3,5 -TPP 3.5 kg / m2, 10 m2
- Ruberoid RPP 300 (15m)
- Imper Standard (T) V - TKP 4.0 kg/m2, 10 m2
PARAMETER ITEM, MEASURE UNIT |
VALUE |
Width, m |
1 |
Length, m |
10 |
Weight, kg/m2 |
5,0 |
Base |
High durability polyester |
Breaking load under tension, N/50 mm, not less |
1000 |
relative elongation, %, not lower |
45 |
Heat resistance during two hours at the temperature of °С, not lower |
110 |
Radius of curvature with radius at bent 25 mm at the temperature of °С, not above |
- 30 |
Ductile-to-brittle transition temperature of polymeric-bitumen binder at the temperature of °С, not above |
- 40 |
Waterproofing under a pressure 0.2 MPa, not lower, during 24 hours |
No signs of water leak |
Water absorption during 24 hours by weight, %, not above |
1 |